Home / Products  / Industrial Program / Rubber lining for corrosion protection / CHEMOLINE – soft rubber lining
Rubber lining for corrosion protection
CHEMOLINE – soft rubber lining
CHEMOLINE 3
Properties

  • Good chemical resistance to mineral acids, bases and aqueous liquors
  • Good abrasion resistance to aggressive media with high content of solids


   Area of application

Lining for
  • Pipe spools
  • Stirrer vessels
  • Storage containers
  • Road tank cars
  • Railway tank cars
  • Ship cargo holds
CHEMOLINE 3/CN
Polychloroprene material with "sticky-back" CN bonding layer.
Bonding with Metal Primer PR 304 / Cement BC 3004 or Metal Primer PR 300 / Cement BC 3000.
Polymer basis
Polychloroprene rubber (CR)
Specific weight
1.44 g/cm³DIN EN ISO 1183
Hardness
55 ± 5 Shore AISO 868-2003 (DIN 53505)
Abrasion
max. 200 mm³DIN ISO 4649-2006
Resilience
min. 25%ISO 4462-1986 (DIN 53512)
Max. temperature
max. 85°C
Roll length
10 m (width 1 100 mm)
Color
Black
Ref. No. Designation Weight Thickness
5287835
CHEMOLINE 3/CN 3.02 kg/m²
2 mm
5287842
CHEMOLINE 3/CN 4.53 kg/m²
3 mm
5287859
CHEMOLINE 3/CN 6.04 kg/m²
4 mm
5287866
CHEMOLINE 3/CN 7.55 kg/m²
5 mm
5287873
CHEMOLINE 3/CN 9.06 kg/m²
6 mm
top
CHEMOLINE 3
Polychloroprene material that may be vulcanised in the shop with hot air or steam in an autoclave or can self-vulcanise on-site within 2-3 months at ambient temperature (T >+ 25 °C).
Bonding with Metal Primer PR 300 / Cement BC 3000 or Metal Primer PR 304 / Cement BC 3004 (CFC-free adhesive system).
Polymer basis
Polychloroprene rubber (CR)
Specific weight
1.44 g/cm³DIN EN ISO 1183
Hardness
55 ± 5 Shore AISO 868-2003 (DIN 53505)
Abrasion
max. 200 mm³DIN ISO 4649-2006
Resilience
min. 25%ISO 4462-1986 (DIN 53512)
Max. temperature
max. 85°C
Roll length
10 m (width 1 100 mm)
Color
Black
Ref. No. Designation Weight Thickness
5282531
CHEMOLINE 3 3.03 kg/m²
2 mm
5282579
CHEMOLINE 3 4.54 kg/m²
3 mm
5282610
CHEMOLINE 3 6.05 kg/m²
4 mm
5282658
CHEMOLINE 3 7.56 kg/m²
5 mm
5282696
CHEMOLINE 3 9.08 kg/m²
6 mm
top
CHEMOLINE 4
Properties

  • Excellent diffusion resistance to gases such as sulfur dioxide, nitrogen oxides and saturated water vapour
  • Outstanding chemical resistance to mineral acids, bases, aqueous phases and polar solvents
  • Weatherproof


   Area of application

Lining for
  • Crystallisers
  • Flue gas desulfurisation plants
  • Pickling baths
  • Pipe spools
  • Storage containers
  • Road tank cars
  • Railway tank cars
  • Ship cargo holds
CHEMOLINE 4/CN
Pre-cured bromobutyl material with "sticky-back" CN bonding layer.
General Technical Approval Z.59.22-149 from DIBt.

Bonding with Metal Primer PR 304 / Cement BC 3004 or Metal Primer PR 300 / Cement BC 3000.
Polymer basis
Bromobutyl rubber (BIIR)
Specific weight
1.27 g/cm³DIN EN ISO 1183
Hardness
50 ± 5 Shore AISO 868-2003 (DIN 53505)
Abrasion
max. 320 mm³DIN ISO 4649-2006
Resilience
min. 6%ISO 4462-1986 (DIN 53512)
Max. temperature
max. 85°C
Roll length
10 m (width 1 100 mm)
Color
Black
Ref. No. Designation Weight Thickness
5287897
CHEMOLINE 4/CN 4.14 kg/m²
3 mm
5287907
CHEMOLINE 4/CN 5.47 kg/m²
4 mm
5287914
CHEMOLINE 4/CN 6.80 kg/m²
5 mm
5287921
CHEMOLINE 4/CN 8.14 kg/m²
6 mm
top
CHEMOLINE 4 A
Un-vulcanised bromobutyl material, to be vulcanised in an autoclave.
General Technical Approval Z-59.22-162 from DIBt.

Applied with the two-layer primer system Primer PR 500-1 / Primer S 500-2 and bonding solution Cement TC 5000.
Polymer basis
Bromobutyl rubber (BIIR)
Specific weight
1.27 g/cm³DIN EN ISO 1183
Hardness
50 ± 5 Shore AISO 868-2003 (DIN 53505)
Abrasion
max. 320 mm³DIN ISO 4649-2006
Resilience
min. 6%ISO 4462-1986 (DIN 53512)
Max. temperature
max. 100°C
Roll length
10 m (width 1 100 mm)
Color
Black
Ref. No. Designation Weight Thickness
5282720
CHEMOLINE 4 A 2.67 kg/m²
2 mm
5282768
CHEMOLINE 4 A 4.01 kg/m²
3 mm
5282809
CHEMOLINE 4 A 5.34 kg/m²
4 mm
5282847
CHEMOLINE 4 A 6.67 kg/m²
5 mm
5282885
CHEMOLINE 4 A 8.01 kg/m²
6 mm
top
CHEMOLINE 4 B
Uncured bromobutyl material for self-vulcanising construction site applications.
General Technical Approval Z-59.22-159 from DIBt.

Applied with the two-layer primer system Primer PR 500-1 / Primer S 500-2 and bonding solution Cement TC 5000.
Polymer basis
Bromobutyl rubber (BIIR)
Specific weight
1.27 g/cm³DIN EN ISO 1183
Hardness
50 ± 5 Shore AISO 868-2003 (DIN 53505)
Abrasion
max. 320 mm³DIN ISO 4649-2006
Resilience
min. 6%ISO 4462-1986 (DIN 53512)
Max. temperature
max. 100°C
Roll length
10 m (width 1 100 mm)
Color
Black
Vulcanisation requires about 3-4 months at an ambient temperature of 25°C.
Ref. No. Designation Weight Thickness
5282933
CHEMOLINE 4 B 2.67 kg/m²
2 mm
5282971
CHEMOLINE 4 B 4.01 kg/m²
3 mm
5283011
CHEMOLINE 4 B 5.34 kg/m²
4 mm
5283059
CHEMOLINE 4 B 6.67 kg/m²
5 mm
5283097
CHEMOLINE 4 B 8.01 kg/m²
6 mm
top
CHEMOLINE 5
Properties

  • Excellent diffusion resistance to gases such as sulfur dioxide, nitrogen oxides and saturated water vapour
  • Weatherproof
  • Good chemical resistance to mineral acids, bases and aqueous liquors


   Area of application

Lining for
  • Seawater desalination plants
  • Pickling baths
  • Stirrer vessels
  • Filter vessels
  • Slurry tanks
  • Ion exchangers
  • Pipe spools
CHEMOLINE 5 B
Self-vulcanising bromobutyl chloroprene material.

Applied with the two-layer primer system Primer PR 500-1 / Primer S 500-2 and bonding solution Cement TC 5000 with a subsequent thermal treatment.

When the rubber sheet has already begun to vulcanise, bonding on steel is achieved using Metal Primer PR 304 / Cement BC 3004. Alternatively, the adhesive system Metal Primer PR 300 / Cement BC 3000 may be used.
Polymer basis
Bromobutyl chloroprene rubber (BIIR)
Specific weight
1.30 g/cm³DIN EN ISO 1183
Hardness
50 ± 5 Shore AISO 868-2003 (DIN 53505)
Abrasion
max. 225 mm³DIN ISO 4649-2006
Resilience
min. 10%ISO 4462-1986 (DIN 53512)
Max. temperature
up to 90°C.
Roll length
10 m (width 1 100 mm)
Color
black
Ref. No. Designation Weight Thickness
5283334
CHEMOLINE 5 B 2.65 kg/m²
2 mm
5283372
CHEMOLINE 5 B 3.97 kg/m²
3 mm
5283413
CHEMOLINE 5 B 5.30 kg/m²
4 mm
5283451
CHEMOLINE 5 B 6.62 kg/m²
5 mm
5283499
CHEMOLINE 5 B 7.94 kg/m²
6 mm
top
CHEMOLINE 5/CN
Self-vulcanising bromobutyl chloroprene material with "sticky-back" CN bonding layer.

Bonding with Metal Primer PR 304 / Cement BC 3004 or Metal Primer PR 300 / Cement BC 3000.
Polymer basis
Bromobutyl chloroprene rubber (BIIR/CR)
Specific weight
1.30 g/cm³DIN EN ISO 1183
Hardness
50 ± 5 Shore AISO 868-2003 (DIN 53505)
Abrasion
max. 225 mm³DIN ISO 4649-2006
Resilience
min. 10%ISO 4462-1986 (DIN 53512)
Roll length
10 m (width 1 100 mm)
Color
Black
Ref. No. Designation Weight Thickness
5287945
CHEMOLINE 5/CN 4.11 kg/m²
3 mm
5287952
CHEMOLINE 5/CN 5.44 kg/m²
4 mm
5287969
CHEMOLINE 5/CN 6.76 kg/m²
5 mm
5287976
CHEMOLINE 5/CN 8.08 kg/m²
6 mm
top
CHEMOLINE 8
Properties

  • Good chemical resistance to mineral acids, bases and aqueous liquors. Outstanding resistance to media with oxidising effects such as sodium hypochlorite and chromic acid


   Area of application

  • For the chemicals, chloride and steel industry, especially for electroplating
  • For storage and transport containers (lining of road and railway tank cars)
  • Lining of transport containers for transporting varying types of chemicals as well as mixed and used acids
CHEMOLINE 8
Un-vulcanised CSM/PVC material for autoclave or hot-air vulcanisation.
General Technical Approval Z.59.22-234 from DIBt.

Applied with the two-layer primer system Primer HG 1 / Primer HG 2 and bonding solutions Cement TC 6000 and CHEMO 8 SOLUTION.
Polymer basis
Chlorosulfonated polyethylene (CSM) / polyvinylchloride (PVC)
Specific weight
1.20 g/cm³DIN EN ISO 1183
Hardness
73 ± 5 Shore AISO 868-2003 (DIN 53505)
Resilience
min. 20%ISO 4462-1986 (DIN 53512)
Max. temperature
max. 80°C
Roll length
10 m (width 1 100 mm)
Color
Brown
Vulcanisation with autoclaves
Ref. No. Designation Weight Thickness
5283736
CHEMOLINE 8 2.52 kg/m²
2 mm
5283774
CHEMOLINE 8 3.78 kg/m²
3 mm
5283815
CHEMOLINE 8 5.04 kg/m²
4 mm
5283853
CHEMOLINE 8 6.30 kg/m²
5 mm
5283891
CHEMOLINE 8 7.56 kg/m²
6 mm
top
CHEMOLINE 8/CN
Pre-vulcanised CSM/PVC material with "sticky-back" CN bonding layer.

Bonding with Metal Primer PR 304 / Cement BC 3004 or Metal Primer PR 300 / Cement BC 3000.
Polymer basis
Chlorosulfonated polyethylene (CSM) / polyvinylchloride (PVC)
Specific weight
1.20 g/cm³DIN EN ISO 1183
Hardness
65 ± 5 Shore AISO 868-2003 (DIN 53505)
Resilience
min. 20%ISO 4462-1986 (DIN 53512)
Max. temperature
max. 80°C
Roll length
10 m (width 1 100 mm)
Color
Black
Ref. No. Designation Weight Thickness
5288047
CHEMOLINE 8/CN 3.97 kg/m²
3 mm
5288054
CHEMOLINE 8/CN 5.23 kg/m²
4 mm
5288061
CHEMOLINE 8/CN 6.49 kg/m²
5 mm
5288078
CHEMOLINE 8/CN 7.75 kg/m²
6 mm
top
CHEMOLINE 10
Properties

  • Excellent diffusion resistance to gases such as sulfur dioxide, nitrogen oxides and saturated water vapour
  • Good chemical resistance to mineral acids, bases and aqueous liquors


   Area of application

Lining for
  • Seawater desalination plants
  • Flue gas desulfurisation systems
  • Stirrer vessels
  • Filter vessels
  • Slurry tanks
CHEMOLINE 10
Polymer basis
Chlorobutyl-chloroprene rubber (CIIR/CR)
Specific weight
1.24 g/cm³DIN EN ISO 1183
Hardness
65 ± 5 Shore AISO 868-2003 (DIN 53505)
Resilience
min. 8%ISO 4462-1986 (DIN 53512)
Max. temperature
max. 85°C
Roll length
10 m (width 1 100 mm)
Color
Black
Ref. No. Designation Weight Thickness
5283963
CHEMOLINE 10 2.78 kg/m²
2 mm
5283970
CHEMOLINE 10 4.17 kg/m²
3 mm
5284230
CHEMOLINE 10 5.56 kg/m²
4 mm
5284247
CHEMOLINE 10 6.95 kg/m²
5 mm
5284254
CHEMOLINE 10 8.33 kg/m²
6 mm
top
CHEMOLINE 55
Properties

  • Outstanding resistance to chemicals with moderate concentrations and high solid contents
  • Resists abrasion


   Area of application

  • Lining of plant components in ore dressing and fertiliser industries
CHEMOLINE 55
Un-vulcanised NR material that can be vulcanised in the workshop with pressurised steam (autoclave).

Applied with the two-layer primer system Primer PR 500-1 / Primer S 500-2 and bonding solution REMACLAVE Solution.
Polymer basis
Natural rubber
Specific weight
1.13 g/cm³DIN EN ISO 1183
Hardness
55 ± 5 Shore AISO 868-2003 (DIN 53505)
Abrasion
up to 100 mm³DIN ISO 4649-2006
Resilience
from 63%ISO 4462-1986 (DIN 53512)
Roll length
10 m (width 1 100 mm)
Color
Black
Ref. No. Designation Weight Thickness
5283925
CHEMOLINE 55 3.56 kg/m²
3 mm
5283932
CHEMOLINE 55 4.75 kg/m²
4 mm
5283949
CHEMOLINE 55 5.94 kg/m²
5 mm
5283956
CHEMOLINE 55 7.12 kg/m²
6 mm
top
CHEMOLINE 55/CN
Pre-vulcaniesd NR material with "sticky-back" CN bonding layer.

The lining material CHEMOLINE 55/CN is bonded onto steel with Metal Primer PR 304 in combination with Cement BC 3004. Alternatively, the adhesive system Metal Primer PR 300 / Cement BC 3000 may be used.
Polymer basis
Natural rubber
Specific weight
1.13 g/cm³DIN EN ISO 1183
Hardness
55 ± 5 Shore AISO 868-2003 (DIN 53505)
Abrasion
up to 100 mm³DIN ISO 4649-2006
Resilience
from 63%ISO 4462-1986 (DIN 53512)
Roll length
10 m
Color
Black
Ref. No. Designation Weight Thickness
5289895
CHEMOLINE 55/CN 3,81 kg/m²
3 mm
5289905
CHEMOLINE 55/CN 5.0 kg/m²
4 mm
5289912
CHEMOLINE 55/CN 6.19 kg/m²
5 mm
5283956
CHEMOLINE 55/CN 7.37 kg/m²
6 mm
top
CHEMOLINE 61
Properties

  • Good chemical resistance to mineral acids, bases and aqueous liquors. Outstanding resistance to media with oxidising effects such as sodium hypochlorite and chromic acid


   Area of application

  • For the chemicals, chloride and steel industry, especially for electroplating
  • For acid picking baths and electroplating baths
CHEMOLINE 61
Un-vulcanised butyl rubber/PVC material for autoclave vulcanisation or hot-air vulcanisation
Polymer basis
Butyl rubber (IIR) / Polyvinylchloride (PVC)
Specific weight
1.18 g/cm³DIN EN ISO 1183
Hardness
62 ± 5 Shore AISO 868-2003 (DIN 53505)
Resilience
from 12%ISO 4462-1986 (DIN 53512)
Max. temperature
up to 80°C
Roll length
10 m (width 1 100 mm)
Color
Black
Vulcanisation with autoclaves
Ref. No. Designation Weight Thickness
5282036
CHEMOLINE 61 2.48 kg/m²
2 mm
5282074
CHEMOLINE 61 3.72 kg/m²
3 mm
5282115
CHEMOLINE 61 4.96 kg/m²
4 mm
5282153
CHEMOLINE 61 6.20 kg/m²
5 mm
5282191
CHEMOLINE 61 7.44 kg/m²
6 mm
top
CHEMOLINE 61/CN
Pre-vulcanised IIR/PVC material with "sticky-back" CN bonding layer
Polymer basis
Butyl rubber (IIR)/ Polyvinylchloride (PVC)
Specific weight
1.18 g/cm³DIN EN ISO 1183
Hardness
62 ± 5 Shore AISO 868-2003 (DIN 53505)
Resilience
from 12%ISO 4462-1986 (DIN 53512)
Max. temperature
up to 80°C
Roll length
10 m (width 1 100 mm)
Color
Black
Ref. No. Designation Weight Thickness
5282200
CHEMOLINE 61/CN 2.69 kg/m²
2 mm
5282210
CHEMOLINE 61/CN 3,93 kg/m²
3 mm
5282220
CHEMOLINE 61/CN 5.17 kg/m²
4 mm
5282230
CHEMOLINE 61/CN 6.41 kg/m²
5 mm
5282240
CHEMOLINE 61/CN 7.64 kg/m²
6 mm
top
CHEMOLINE 70
Properties

  • Outstanding resistance to hydrochloric acid (HCI) up to maximum concentration
  • Good chemical resistance to mineral acids, bases and aqueous liquors


   Area of application

Lining for
  • Acid pickling baths and electroplating baths
  • Tanks for manufacturing, storing and regeneration of hydrochloric acid
CHEMOLINE 70/CN
Pre-vulcanised chlorobutyl rubber material with "sticky-back" CN bonding layer.

Bonding with Metal Primer PR 304 / Cement BC 3004 or Metal Primer PR 300 / Cement BC 3000.
Polymer basis
Chlorobutyl rubber and PVC (CIIR/PVC)
Specific weight
1.17 g/cm³DIN EN ISO 1183
Hardness
57 ± 5 Shore AISO 868-2003 (DIN 53505)
Roll length
10 m (width 1 100 mm)
Color
Black
Ref. No. Designation Weight Thickness
5288140
CHEMOLINE 70/CN 3.90 kg/m²
3 mm
5288157
CHEMOLINE 70/CN 5.13 kg/m²
4 mm
5288164
CHEMOLINE 70/CN 6.36 kg/m²
5 mm
5288171
CHEMOLINE 70/CN 7.59 kg/m²
6 mm
top